Storage:

• The storage temperature should not exceed 35 ℃.
• Keep tightly closed. Store in a cool, dry, well-ventilated area.
• Do not expose to ultraviolet light.
• High temperatures (>80 ℃), pressure and contamination with peroxides may result in auto-polymerization of the product.
• Unstable upon depletion of inhibitor.

UV curable very low viscosity resin:

• Cures rapidly to form a glassy, high modulus material.
• Excellent for use in applications requiring low viscosity, high hardness, and low shrinkage stress.
• Good for some spray coatings requiring no volatile organic compounds (VOCS).
• Non-yellowing.
• Low oxygen inhibition.
• Mechanical properties after curing:

Modulus*: 750 MPa
Strength*: 20 MPa
Elongation*: 11%
Pencil Hardness: 6H
Tack free**: 35

*Test resources: Tensile tester, 35 mm gauge length, 1.0 mm thickness, 6.5 mm width.
** Cured under stated intensity. Medium pressure mercury bulb with 320-500 nm filter. Adhesion tests were conducted using a cross hatch tape test on films 0.125 mm thick on glass and PET. Material Data using ASTM D 638-02a.

100

liquid (colorless)

55 cP (Brookfield LDTDV-II digital viscometer with size 31 spindle)

flash point >110 ℃

1.16 g/mL

2-8℃

250 g in poly bottle

GHS07,GHS09

Warning

H315 - H317 - H319 - H335 - H411

P261 - P264 - P273 - P280 - P302 + P352 - P305 + P351 + P338

Aquatic Chronic 2 - Eye Irrit. 2 - Skin Irrit. 2 - Skin Sens. 1 - STOT SE 3

Respiratory system

10 - Combustible liquids

WGK 3