UV 固化树脂

NA.23

Storage:

• The storage temperature should not exceed 35℃.
• Keep tightly closed. Store in a cool, dry, well ventilated area.
• Do not expose to ultraviolet light.
• High temperatures (>80℃), pressure and contamination with peroxides may result in auto-polymerization of the product.
• Unstable upon depletion of inhibitor.

• UV curable very low viscosity resin.
• Cures rapidly to form a glassy high modulus material.
• Excellent for use in applications requiring low viscosity, high hardness and low shrinkage stress.
• Good for some spray coatings requiring no volatile organic compounds (VOCS).
• Non yellowing.
• Low oxygen inhibition.
• Mechanical properties after curing:

Modulus*: 840 MPa
Strength*: 23 MPa
Elongation*: 8%
Pencil hardness: 6H
Tack free**: 80+

*Test Resources: tensile tester, 35 mm gauge length, 1.0 mm thickness, 6.5 mm width.
** Cured under stated intensity. Medium pressure mercury bulb with 320-500 nm filter. Adhesion tests were conducted using a cross hatch tape test on films 0.125 mm thick on glass and PET. Material Data using ASTM D 638-02a.

100

liquid

70 cP (Brookfield LDTDV-II digital viscometer with size 31 spindle)

1.18 g/mL

2-8℃

250 g in poly bottle

GHS05,GHS07,GHS09

Danger

H314 - H317 - H335 - H411

P261 - P271 - P273 - P280 - P303 + P361 + P353 - P305 + P351 + P338

Aquatic Chronic 2 - Eye Dam. 1 - Skin Corr. 1B - Skin Sens. 1 - STOT SE 3

Respiratory system

8A - Combustible, corrosive hazardous materials

WGK 3