紫外-可见光固化树脂

NA.23

Storage:

• The storage temperature should not exceed 35 ℃.
• Keep tightly closed. Store in a cool, dry, well-ventilated area.
• Do not expose to ultraviolet light.
• High temperatures (>80 ℃), pressure and contamination with peroxides may result in auto-polymerization of the product.
• Unstable upon depletion of inhibitor.

• Cures extremely rapidly to form a glassy, high modulus material.
• Excellent for use in optical applications.
• High refractive index - 1.54.
• High impact absorption.
• Non-yellowing.
• No oxygen inhibition.
• Mechanical Properties after curing:

Modulus*: 208 MPa
Strength*: 7 MPa
Elongation*: 54%
Pencil Hardness: 6H
Tack Free**: 3 min

*Test resources: Tensile tester, 35mm gauge length, 1.0 mm thickness, 6.5 mm width.
** Cured under stated intensity. Medium pressure mercury bulb with 320-500 nm filter. Adhesion tests were conducted using a cross hatch tape test on films 0.125 mm thick on glass and PET. Material Data using ASTM D 638-02a.

100

liquid (colorless)

340 cP (Brookfield LDTDV-II digital viscometer with size 31 spindle)

flash point 110 °F

1.22 g/mL

2-8℃

250 g in poly bottle

GHS05,GHS07,GHS08,GHS09

Danger

H302 - H314 - H317 - H373 - H410

P273 - P280 - P301 + P312 - P303 + P361 + P353 - P305 + P351 + P338 - P314

Acute Tox. 4 Oral - Aquatic Acute 1 - Aquatic Chronic 1 - Eye Dam. 1 - Skin Corr. 1B - Skin Sens. 1 - STOT RE 2

8A - Combustible, corrosive hazardous materials

WGK 3

230.0 °F

110 ℃